It contains 17 single masses as well as special liquids and accessories. The 2D and 3D pastes and stains were specially developed for the professional aesthetic finalization of the ceramic restorations.

Contact us


  • Features
  • Accessories
  • Tech Specs
  • Query Information
Features of Blossom

It can be the ALL-in-One supporting all types of ceramic restorations specialized for dental zirconia and lithium Disilicate etc. No need other different pastes.

  • aaa
    Good Surface Finishing

    Surface finishing may involve polishing or staining and glazing, and is the last step when processing your CAD/CAM restoration before cementation. It is this process that will give your restoration a high shine appearance which is desirable for aesthetic and hygienic reasons.

  • aaa
    Smooth restoration

    Bacteria don't adhere to a smooth surface nearly as much as a rough surface, and it is also easier to clean for your patient. On top of that your restoration will have better colour stability long term as it doesn't stain as much.

  • aaa
    Glaze gradation more natural

    The glaze paste performance is extremely matched with natural teeth.

Accessories for Blossom

Paste 2D Body A: 3 grams

Paste 2D Body B: 3 grams

Paste 2D Body C: 3 grams

Paste 2D Body D: 3 grams

Paste 2D White: 3 grams

Paste 2D Blue: 3 grams

Paste Glaze: 3 grams

Paste 2D Body Red+: 3 grams

Paste 2D Body Orange: 3 grams

Paste 2D Body L: 3 grams

Paste 2D Grey: 3 grams

Paste 2D Violet: 3 grams

Paste 2D Incisal I2: 3 grams

Paste 3D Transparent: 3 grams

Paste 3D Dentin Bleach: 3 grams

Stain 1 White: 3 grams

Stain 12 Red Brown: 3 grams

2D Brush: 1 pc

3D Brush: 1 pc

Diluting Liquid: 10 ml

Refreshing Liquid: 10 ml

Blossom Technical Specifications
Technical Specifications

Temperature at beginning (°C/°F)450 / 842
Drying time (min)8
Heat rate (°C/°F per m)55 / 131
Vacuum begins (°C/°F)450 / 842
Vacuum ends (°C/°F)730/1346 for 2D, 720/1328 for 2D & 3D
Sintering temperature (°C/°F)730/1346 for 2D, 720/1328 for 2D & 3D
Hold-time (min)1 (without vacuum)
Coefficient of thermal expansionCTE(25 °C/77 °F-Tg)
Flexural strength>50 MPa
Chemical solubility< 100 μg/cm20
Transformation temperature≈ 480 °C - 490 °C (896 °F - 914 °F)