Features of White Zirconia
The preshaded zirconia that covers all 16 shades of the VITA Classic shade guide, With pre-shaded zirconia there is no need for laboratory technicians to shade each unit, saving production time.
Consistent VITA® Classic Shade Match
Strictly follow up VITA® Classic Shade from the R & D phase and also by the standard production with shade match.
Glazed with Bloomden CeramStar Glaze/Stain Kit
Preparation: Multilayer crown bridge after milled and sintered and then glazed.
Incisal Translucency and appearance
The translucency of preshaded zirconia and the additional light refraction from the preshaded zirconia phase results in a natural incisal translucency.
Accessories for White Zirconia
CeramStar® Glaze/StainGingivalSet
It contains 4 single masses as well as special liquids and accessories. The 3D pastes were specially developed for the aesthetic finalization and characterization of the gingival-colored parts of ceramic restorations, made of lithium disilicate and 3D Pro Multilayer. All parts of the set are also available individually.
LEARN MORE
CeramStar® Glaze/Stain Vivid Set
It contains 7 single masses as well as special liquids and accessories. The 2D pastes were specially developed for the basic aesthetic finalization of the ceramic restorations, made of lithium disilicate and 3D Pro Multilayer. All parts of the set are also available individually.
LEARN MORE
CeramStar® Glaze/Stain Blossom Set
It contains 17 single masses as well as special liquids and accessories. The 2D and 3D pastes and stains were specially developed for the professional aesthetic finalization of ceramic restorations, made of lithium disilicate and 3D Pro Multilayer. All parts of the set are also available individually.
LEARN MORE
White Zirconia Technical Specifications
| Technical Specifications | ||||
|---|---|---|---|---|
| UT | HT-PLUS | ST | SHT | |
| ZrO2+HfO2+Y2O3 | ≥99% | ≥99% | ≥99% | ≥99% |
| Y2O3 | 9%-10% | 4.5%-6.0% | 4.5%-6.0% | 7.0%-7.8% |
| Al2O3 | ＜0.05% | ＜0.15% | ＜0.15% | ＜0.15% |
| Density before sintering (g.cm-3) | 3.20±0.05 | 3.15±0.05 | 3.15±0.05 | 3.15±0.05 |
| Density after sintering (g.cm-3) | 6.06±0.01 | 6.09±0.01 | 6.09±0.01 | 6.08±0.01 |
| CTE (25-500°C) (K-1) | 10.5±0.5 | 10.5±0.5 | 10.5±0.5 | 10.5±0.5 |
| Flexural strength after sintering (MPa) | ＞600 | ＞1350 | ＞1200 | ＞1000 |
| Aging surface monoclinic phase content | ＜15% | ＜15% | ＜15% | ＜15% |
| Light transmittance | ＜49% | <37% | 41%-43% | ＜46% |
| Chemical solubility after sintering (µg.cm-2) | ＜100 | ＜100 | ＜100 | ＜100 |
| Cytotoxicity | 0 Level | 0 Level | 0 Level | 0 Level |
| Radioactivity (Bq.g-1) | ＜0.1 | ＜0.1 | ＜0.1 | ＜0.1 |
| Sintering temperature (°C) | 1450 | 1530 | 1530 | 1530 |
| Systems | 98mm / 95mm / 92*75mm | |||
| Thickness | 12m / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm | |||
| Shades | A1 A2 A3 A3.5 A4 / B1 B2 B3 B4 / C1 C2 C3 C4 / D2 D3 D4 | |||